产品特性
The characteristics of the product
l 固化后的材料具有较高的强度，可进行各类机械加工
L cured materials with high strength, can be all kinds of mechanical processing
l 与金属具有较高的结合强度
L and metal with high bonding strength
l 修补后的颜色与基材基本一致
Color and material l repair after basic consistent
l 应用范围广，适用于各种金属材质缺陷的修补和再生
L has wide application range, repair and regeneration is applicable to all kinds of metal material defects
l 具有耐磨抗蚀与耐老化的特性
L has the characteristics of wear resistance and corrosion resistance and aging resistance
多金属修补剂系列产品
Multi metal repairing agent series products
101铸造缺陷修补剂
101 the casting defect repair agent
包装规格：500g/组
Packaging specifications: 500g/ group
双组分，通用型。物理状态为膏状，体积303 cm3，操作时限(25℃) 25min，固化时间(25℃) 18h，用于各种铸造缺陷的填补。
Two component, general. Physical state, paste, volume 303 cm3, operation time (25 ℃) 25min, curing time (25 ℃) 18h, used to fill all kinds of casting defects.
111铁质修补剂
111 iron repair agent
包装规格：500g/组
Packaging specifications: 500g/ group
物理状态为膏状，体积309cm3，操作时限(25℃) 45min，固化时间(25℃) 24h，综合机械性能好，特别适合灰铁、球铁等材质，用于铸铁件的修补，如铸造缺陷的填补及零件磨损、腐蚀、破裂的修复。
Physical state, paste, the volume of 309cm3, operation time (25 ℃) 45min, curing time (25 ℃) 24h, the mechanical properties, especially suitable for gray iron, ductile iron and other materials, used for cast iron casting defects repair, such as fill and parts wear and corrosion, fracture repair.
112钢质修补剂
112 steel repair agent
包装规格：500g/组
Packaging specifications: 500g/ group
物理状态为膏状，体积298cm3，操作时限(25℃) 45min，固化时间(25℃) 24h，耐磨性及结合强度高，用于各种碳钢、合金钢、不锈钢的修补。如铸造缺陷的填补及零件磨损、划伤、腐蚀、破裂的修复。
Physical state, paste, the volume of 298cm3, operation time (25 ℃) 45min, curing time (25 ℃) 24h, wear resistance and high bonding strength, for a variety of carbon steel, alloy steel, stainless steel repair. Such as casting filling defect and repair parts wear, corrosion, scratches, rupture.
113铝质修补剂
113 aluminum repair agent
包装规格：250g/组
Packaging specifications: 250g/ group
物理状态为膏状，体积177cm3，操作时限(25℃) 45min，固化时间(25℃)24h，用于各种铸铝件缺陷的修补及铝质零件磨损的修复。
Physical state, paste, the volume of 177cm3, operation time (25 ℃) 45min, curing time (25 ℃) 24h, used in a variety of aluminum casting defect repair and aluminum parts wear repair.
114铜质修补剂
114 copper repairing agent
包装规格：250g/组
Packaging specifications: 250g/ group
物理状态为膏状，体积163 cm3，操作时限(25℃) 45min，固化时间(25℃) 24h，用于黄铜、青铜铸件和工艺铸造件缺陷的修补与再生。
Physical state, paste, Volume 163 cm3, operation time (25 ℃) 45min, curing time (25 ℃) 24h, used to repair and regeneration of the defect of brass, bronze casting and casting processes.
主要物理机械性能
Main physical and mechanical properties
|
item code
|
color
|
density
(g/cm3)
|
compress strength
(kg/cm2)
GB1041-79
|
tensile strength
(kg/cm2)
GB6329-86
|
shear strength
(kg/cm2)
GB7124-86
|
bending strength
(kg/cm2)
GB1042-79
|
hardness
（Shore D）
ASTM-D-2556
|
working temperature
（℃）
|
|
101
|
grey
|
1.66
|
865
|
291
|
181
|
486
|
84
|
-60～120
|
|
111
|
iron
|
1.61
|
977
|
324
|
189
|
563
|
90
|
-60～166
|
|
112
|
stainless steel
|
1.68
|
1064
|
391
|
265
|
582
|
93
|
-60～193
|
|
113
|
alum
|
1.40
|
995
|
334
|
236
|
514
|
86
|
-60～166
|
|
114
|
brass
|
1.52
|
922
|
367
|
273
|
512
|
87
|
-60～166
|
L surface treatment: treat repair surface roughening treatment and clean with cleaning agent.Method of use
l 表面处理：对待修表面进行粗化处理并用清洗剂进行清洗。
l 配制：按产品说明上的比例将A、B两组份混合均匀，并在规定操作期限内用完。
L preparation: according to the description on the proportion of A, B two groups were mixed uniformly, and used in the specified operating period.
l 涂敷：将混合好的材料逐层涂敷于待修部位，第一层要压实，使之与基材充分浸润。如后序需机械加工，要留出适量加工余量。
L coating: the mixed material layer coated on the repair site, the first layer to compaction, so that the full invasion and substrate. If the order need mechanical processing, to set aside appropriate machining allowance.
l 固化：25～30℃固化8小时可以进行机械加工，24小时后投入使用，若温度低应采用加热或延长固化时 间来促进固化。
L curing: 25 ~ 30 ℃ curing for 8 hours can be machined, 24 hours after put into use, if the temperature is low should be used for heating or extend the curing time to promote curing.