Is the antifriction material from various types of high wear resistance, corrosion resistant material or (such as ceramics, silicon carbide, corundum, titanium alloy, MoS2) composite obtained high properties of wear resistance and corrosion resistance of ceramic materials and Polymer Toughened resin. Widely used for the corrosion resistance requirements of parts surface preparation of wear and corrosion resistant coating.
产品特性
The characteristics of the product
l 抗蚀性是一般金属的2倍以上
L corrosion resistance is 2 times more than the general metal
l 与金属类基材具有很高的结合强度
L with metal substrate has high binding strength
l 施工方便，对施工人员无很高技术要求
L construction is convenient, no high requirements on the construction personnel
l 适用于多种腐蚀工况的修复和防护
Repair and protection of L is applicable to a variety of corrosion condition
耐腐蚀修补剂系列产品
Corrosion resistant repair agent series products
406耐腐蚀修补剂
406 corrosion resistant repair agent
包装规格：500g/组
Packaging specifications: 500g/ group
物理状态为膏状，体积364cm3，操作时限(25℃) 45min，可使用时间(25℃) 24h，修补各类遭受常温腐蚀的泵、阀、管路、热交换器端板、叶片并可进行大面积预保护。
Physical state, paste, the volume of 364cm3, operation time (25 ℃) 45min, can use the time (25 ℃) 24h, repair all kinds of suffering corrosion pump, valve, pipe, heat exchanger end plate, the blade and a large area can be pre protection.
416耐腐蚀修补剂
416 corrosion resistant repair agent
包装规格：250g/组
Packaging specifications: 250g/ group
物理状态为膏状，体积182cm3，操作时限(25℃) 45min，可使用时间(25℃) 24h，局部修复遭受腐蚀的泵、阀、管路、热交换器端板、化工泵及叶片、酸碱贮罐、化工管道等。
Physical state, paste, the volume of 182cm3, operation time (25 ℃) 45min, can use the time (25 ℃) 24h, local repair of corrosion pump, valve, pipe, heat exchanger end plate, chemical pumps and vane, acid-base tank, piping etc..
主要物理机械性能
Main physical and mechanical properties
|
item code
|
color
|
density
(g/cm3)
|
compress impact
(kg/cm2)
GB1041-79
|
tensile strength
(kg/cm2)
GB6329-86
|
shear strength
(kg/cm2)
GB7124-86
|
bending strength
(kg/cm2)
GB1042-79
|
hardness
（Shore D）
ASTM-D-2556
|
relative wear resistanceβ（steel:1） or coefficient of friction.μ
GB3960-83
|
working temperature
（℃）
|
|
406
|
blue
|
1.38
|
1004
|
353
|
254
|
562
|
86
|
β:1.9
|
-60～150
|
|
416
|
grey
|
1.37
|
1113
|
337
|
233
|
543
|
88
|
β:2.2
|
-60～150
|
Method of use
l 表面处理：对待修补部位进行粗化处理，如条件允许可车出1.5mm深的缧纹，再用清洗剂进行清洗。
L surface treatment: treat repair parts for rough treatment, if conditions allow can car 1.5mm deep microgroove, cleaning and cleaning agent.
l 配制：按说明上的比例将A、B两组份混合均匀，并在规定操作期限内用完。
L preparation: follow the instructions on the ratio of A, B two groups were mixed uniformly, and used in the specified operating period.
l 涂敷：将混合好的材料逐层涂敷于待修部位，第一层要压实，使之与基材充分浸润。如后序需机械加工，要留出适量加工余量。
L coating: the mixed material layer coated on the repair site, the first layer to compaction, so that the full invasion and substrate. If the order need mechanical processing, to set aside appropriate machining allowance.
l 固化：25～30℃固化8小时可以进行机械加工，24小时后可投入使用，若温度低应采用加热或延长固化时间来促进固化。
L curing: 25 ~ 30 ℃ curing for 8 hours can be machined, 24 hours after being put into use, if the temperature is low heat or extend the curing time should be used to promote the curing.